Effect of dioctyl phathalate modified matriz on the thermal stability of glass fiber reinforced c...

1. Modification of polyester

1.1. Prepared by measuring 150ml, initiator and 3 min

1.2. cobalt accelerator 2 min, removed 24h later

1.3. considered as unmodified

2. Production of composite materials

2.1. coposite prepared with matrix modified

2.2. results compared

2.3. mould convered and transferred to a carver lab

3. Thermal analysis

3.1. Carried out using 25 mg

3.2. test conducted at heating rate of 10°C/min

3.3. % wiight loss at various temperatures was recorded

4. Experimental

4.1. General purpose Polyester

4.2. Glass Fiber